A-A-51155C
2.4 Class. The class to be furnished shall be as specified (see 7.3(f)). Unless otherwise specified (see 7.3(g)), the spacing of teeth along the circumference of the cutter head shall be selected from table III or IV for the diameter of the cutter head.
TABLE III. Type I rotary files, number of teeth per circumference.
Cutting head diameter (inch) |
Teeth per circumference |
|||
Class A coarse cut |
Class B medium cut |
Class C fine cut |
Class D extra coarse cut |
|
3/16 |
9 - 11 |
12 - 14 |
15 - 20 |
4 - 8 |
1/4 |
10 - 13 |
14 - 16 |
17 - 21 |
4 - 9 |
3/8 |
12 - 17 |
18 - 22 |
23 - 30 |
5 - 11 |
1/2 |
14 - 20 |
21 - 26 |
27 - 35 |
7 - 13 |
5/8 |
17 - 22 |
23 - 29 |
30 - 40 |
9 - 16 |
3/4 |
18 - 24 |
25 - 32 |
33 - 44 |
10 - 17 |
1 |
20 - 27 |
28 - 41 |
42 - 55 |
14 - 19 |
TABLE IV. Type II rotary files, number of teeth per circumference.
Cutting head diameter (inch) |
Teeth per circumference |
|||
Class A coarse cut |
Class B medium cut |
Class C fine cut |
Class D extra coarse cut |
|
1/8 |
8 - 11 |
12 - 15 |
16 - 20 |
4 - 7 |
1/4 |
12 - 15 |
16 - 20 |
21 - 26 |
4 - 11 |
3/8 |
13 - 18 |
19 - 26 |
27 - 38 |
5 - 12 |
1/2 |
16 - 22 |
23 - 28 |
29 - 39 |
7 - 15 |
5/8 |
18 - 25 |
26 - 38 |
39 - 47 |
9 - 17 |
3/4 |
19 - 28 |
29 - 38 |
39 - 49 |
14 - 18 |
3. SALIENT CHARACTERISTICS
3.1 General requirements.
3.1.1 Type I rotary files. The cutting heads of type I rotary files shall meet the minimum requirements for standard high-speed steel described in the annex of ASTM A 600, "Standard Specification for Tool Steel High Speed", when tested in accordance with ASTM A 370, "Standard Test Methods and Definitions for Mechanical Testing of Steel Products".
3.1.2 Type II rotary files. The cutting heads of type II rotary files shall be manufactured from tungsten carbide with a hardness of not less than 91.2 and not greater than 92.5 on the Rockwell "A" scale when tested in accordance with ASTM B 294, "Standard Test Method for Hardness Testing of Cemented Carbides". The cutting heads of type II rotary files shall have a density of
14.6 to 15.1 grams per cubic centimeter when tested in accordance with ASTM B 311, "Test